Al & Fe Properties

The document provides information on the properties of four metal alloys: 1) Wrought aluminum-silicon alloy 4343 with 7.5% silicon content, density of 2.68 g/cm3, thermal expansion of 21.6x10-6 /°C, and thermal conductivity of 180 W/(mK). 2) Wrought aluminum-silicon alloy 4045 with 10% silicon, density of 2.67 g/cm3, thermal expansion of 21.1x10-6 /°C, and thermal conductivity of 171 W/(mK). 3) Grey cast iron ASTM 40 with carbon content of 2.7-4%, density of 7.06-

Uploaded by

Suhas Mv
Copyright
© Attribution Non-Commercial (BY-NC)
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as DOCX, PDF, TXT or read online on Scribd
45 views3 pages

Al & Fe Properties

The document provides information on the properties of four metal alloys: 1) Wrought aluminum-silicon alloy 4343 with 7.5% silicon content, density of 2.68 g/cm3, thermal expansion of 21.6x10-6 /°C, and thermal conductivity of 180 W/(mK). 2) Wrought aluminum-silicon alloy 4045 with 10% silicon, density of 2.67 g/cm3, thermal expansion of 21.1x10-6 /°C, and thermal conductivity of 171 W/(mK). 3) Grey cast iron ASTM 40 with carbon content of 2.7-4%, density of 7.06-

Uploaded by

Suhas Mv
Copyright
© Attribution Non-Commercial (BY-NC)
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as DOCX, PDF, TXT or read online on Scribd

Wrought aluminum-silicon alloy 4343 Chemical composition: Si=7.5%, Al balance Property Density Value in metric unit 2.

68 *10 kg/m Value in US unit 167 lb/ft

Thermal expansion (20 C) 21.6*10-6 C Thermal conductivity Electric resistivity Liquidus temperature Solidus temperature 180 4.16*10 613 577
-8

12.0*10-6 in/(in* F) 1250 4.16*10 1135 1070


-6

W/(m*K) Ohm*m C C

BTU*in/(hr*ft*F) Ohm*cm F F

Wrought aluminum-silicon alloy 4045 Chemical composition: Si=10.0%, Al balance Property Density Thermal expansion (20 C) Thermal conductivity Electric resistivity Liquidus temperature Solidus temperature Value in metric unit 2.67 *10 21.1*10-6 171 3.82*10-8 599 574 kg/m C W/(m*K) Ohm*m C C 167 11.7*10-6 1190 3.82*10-6 1110 1065 Value in US unit lb/ft in/(in* F) BTU*in/(hr*ft*F) Ohm*cm F F

Grey cast iron ASTM 40 Chemical composition: C=2.7-4%, Mn=0.8%, Si=1.8-3%, S=0.07% max, P=0.2% max Property Density Modulus of elasticity Thermal expansion (20 C) Specific heat capacity (25 C) Thermal conductivity Electric resistivity Tensile strength Elongation Shear strength Compressive yield strength Fatigue strength Hardness (Brinell) Wear resistance Corrosion resistance Weldability Machinability Castability Value in metric unit 7.06 *10-7.34 *10 124 9.0*10-6 490 53.3 1.1*10 276 1 400 Min. 827 138 180-302
-7

Value in US unit 441-458 18000 5.0*10-6 0.117 370 1.1*10


-5

kg/m GPa C J/(kg*K) W/(m*K) Ohm*m MPa % MPa MPa MPa HB

lb/ft ksi in/(in* F) BTU/(lb*F) BTU*in/(hr*ft*F) Ohm*cm psi % psi psi psi HB

40000 1 58000 Min. 120000 20000 180-302 Low Low Low Good High

Ductile cast iron ASTM A536 Chemical composition: C=3.5-3.9%, Mn=0.15-0.35%, Si=2.25-2.75%, S=0.01-0.025%, P=0.05%max Property Density Modulus of elasticity Thermal expansion (20 C) Specific heat capacity Thermal conductivity Electric resistivity Tensile strength Yield strength Elongation Shear strength Fatigue strength Hardness (Brinell) Wear resistance Corrosion resistance Weldability Machinability Castability Shock resistance Value in metric unit 6.64 *10-7.2 *10 172 11.6*10-6 506 32.3 6.0*10-7 496 345 18 372 290 130-217 kg/m GPa C J/(kg*K) W/(m*K) Ohm*m MPa MPa % MPa MPa HB Value in US unit 415-450 lb/ft 25000 ksi

6.46*10-6 in/(in* F) 0.121 224 BTU/(lb*F) BTU*in/(hr*ft*F)

6.0*10-5 Ohm*cm 72000 50000 18 54000 42000 psi psi % psi psi

130-217 HB Low Low Low Good Good Medium