STEEL AUTHORITY OF INDIA LIMITED Page No :A-1 of 1

BHILAI STEEL PLANT IS : 2062

RESEARCH & CONTROL LAB (MECHANICAL TESTING LAB)

TEST CERTIFICATE FOR HOT ROLLED MEDIUM AND HIGH TENSILE STRUCTURAL
STEEL
CM/L-0057534
MTL-II/QR-2

Sold-to-Party: [Link] : RCL/MTL/PLM/80641555

SHREEJEE STRUCTURAL STEEL PVT. LTD. T.C. Date : 30.04.2021
222, GIRIRAJ BUILDING , [Link], SALES ORDER NO : 1100361914
MUMBAI 400009 DA No : 80641555
Ship-to-Party:
SHREEJEE STRUCTURAL STEEL PVT. LTD.,Raigad. Wagon No / Trailer No : SER57071910417
Process of Manufacture of Steel : Basic Oxygen Converter>Continuous Cast>Fully Killed Steel>SiAlK
Specification : IS 2062 E 250 BR : 2011 RA 2016

We certify that the material described below fully conforms to IS 2062 : 2011 RA 2016. Chemical composition and Mechanical properties of the product, as
tested in accordance with the scheme of testing and inspection contained in the BIS certification mark Number CM/L 0057534 are as indicated against each
Order No.
(Please refer to IS 2062 : 2011 RA 2016 for details of specification requirements)
TEST RESULTS

SECTION (NOMINAL SIZE) MECHANICAL PROPERTIES Bend M Dia

Test
THICK WIDTH LENGTH Plate No Heat No YS UTS %E %E2 CHARPY V NOTCH (L) Impact Values (J)
250 MPa 410 MPa Min23(5.6 o
mm mm mm / Pc. No. I1 I2 I3 Iavg C
Min
5SqrtS0)

12 2500 12000 2689133/1 322018 350 530 28 -- -- -- -- -- RT OK 2.0 T

322018 340 492 29 -- 102 96 100 99 RT OK 2.0 T
12 2500 12000 2689137/1 322018 -- -- -- -- -- -- -- -- -- -- --
12 2500 12000 2689138/1 322018 -- -- -- -- -- -- -- -- -- -- --
12 2500 12000 2689138/2 322018 -- -- -- -- -- -- -- -- -- -- --
Heat CHEMICAL COMPOSITION (LADLE ANALYSIS)
N
No C S P Mn Si Al Cu Cr Ni Mo Nb V Ti 2 B CE
% % % % % % % % % % % % % ppm % %
322018 0.17 0.020 0.023 0.90 0.24 0.015 <0.02 <0.015 <0.015 <0.015 <0.010 <0.010 <0.005 -- <0.0005 0.32
Total Pieces Page / Sales Order : 4 / 4 Total Pieces / TC : 15

The Material supplied conforms to the standard rolling and weight tolerances.,
CE calculated by formula: [C + Mn/6 + ( Cr + Mo + V )/5 + ( Ni + Cu )/15 ],
RT- Room temperature as defined in the specification,
Plate sides are in UNTRIMMED condition.,
Size of impact test specimen:10x10x55 mm(above 10mm thickness) ; 7.5x10x55 mm(upto 10mm thickness),
Note:**M = Mandrel Dia, T = Plate Thickness, Length is the rolling direction of the plate,
TC as per BSEN 10204 Type 3.1,

SHARAD KUMAR SAHU

Authorized Signatory
Authorised Signatory Research & Control Laboratory, Bhilai Steel Plant
SAIL/ CMO/ BSO
 STEEL AUTHORITY OF INDIA LIMITED Page No :B-1 of 1
BHILAI STEEL PLANT IS : 2062
RESEARCH & CONTROL LAB (MECHANICAL TESTING LAB)

TEST CERTIFICATE FOR HOT ROLLED MEDIUM AND HIGH TENSILE STRUCTURAL
STEEL
CM/L-0057534
MTL-II/QR-2

Sold-to-Party: [Link] : RCL/MTL/PLM/80641555

SHREEJEE STRUCTURAL STEEL PVT. LTD. T.C. Date : 30.04.2021
222, GIRIRAJ BUILDING , [Link], SALES ORDER NO : 1100365324
MUMBAI 400009 DA No : 80641555
Ship-to-Party:
SHREEJEE STRUCTURAL STEEL PVT. LTD.,Raigad. Wagon No / Trailer No : SER57071910417
Process of Manufacture of Steel : Basic Oxygen Converter>Continuous Cast>Fully Killed Steel>SiAlK
Specification : IS 2062 E 250 BR : 2011 RA 2016

We certify that the material described below fully conforms to IS 2062 : 2011 RA 2016. Chemical composition and Mechanical properties of the product, as
tested in accordance with the scheme of testing and inspection contained in the BIS certification mark Number CM/L 0057534 are as indicated against each
Order No.
(Please refer to IS 2062 : 2011 RA 2016 for details of specification requirements)
TEST RESULTS

SECTION (NOMINAL SIZE) MECHANICAL PROPERTIES Bend M Dia

Test
THICK WIDTH LENGTH Plate No Heat No YS UTS %E %E2 CHARPY V NOTCH (L) Impact Values (J)
240 MPa 410 MPa Min23(5.6 o
mm mm mm / Pc. No. I1 I2 I3 Iavg C
Min
5SqrtS0)

40 1600 12500 2688753/1 324886 328 478 25 -- 88 102 98 96 RT OK 3.0 T

324886 340 488 25 -- -- -- -- -- -- OK 3.0 T
40 1600 12500 2688769/1 324886 -- -- -- -- -- -- -- -- -- -- --
Heat CHEMICAL COMPOSITION (LADLE ANALYSIS)
N
No C S P Mn Si Al Cu Cr Ni Mo Nb V Ti 2 B CE
% % % % % % % % % % % % % ppm % %
324886 0.19 0.007 0.015 0.88 0.24 0.013 <0.02 <0.015 <0.015 <0.015 <0.010 <0.010 <0.005 -- <0.0005 0.34
Total Pieces Page / Sales Order : 2 / 2 Total Pieces / TC : 15

The Material supplied conforms to the standard rolling and weight tolerances.,
CE calculated by formula: [C + Mn/6 + ( Cr + Mo + V )/5 + ( Ni + Cu )/15 ],
RT- Room temperature as defined in the specification,
Plate sides are in UNTRIMMED condition.,
Size of impact test specimen:10x10x55 mm(above 10mm thickness) ; 7.5x10x55 mm(upto 10mm thickness),
Note:**M = Mandrel Dia, T = Plate Thickness, Length is the rolling direction of the plate,
TC as per BSEN 10204 Type 3.1,

SHARAD KUMAR SAHU

Authorized Signatory
Authorised Signatory Research & Control Laboratory, Bhilai Steel Plant
SAIL/ CMO/ BSO
 STEEL AUTHORITY OF INDIA LIMITED Page No :C-1 of 1
BHILAI STEEL PLANT IS : 2062
RESEARCH & CONTROL LAB (MECHANICAL TESTING LAB)

TEST CERTIFICATE FOR HOT ROLLED MEDIUM AND HIGH TENSILE STRUCTURAL
STEEL
CM/L-0057534
MTL-II/QR-2

Sold-to-Party: [Link] : RCL/MTL/PLM/80641555

SHREEJEE STRUCTURAL STEEL PVT. LTD. T.C. Date : 30.04.2021
222, GIRIRAJ BUILDING , [Link], SALES ORDER NO : 1100367963
MUMBAI 400009 DA No : 80641555
Ship-to-Party:
SHREEJEE STRUCTURAL STEEL PVT. LTD.,Raigad. Wagon No / Trailer No : SER57071910417
Process of Manufacture of Steel : Basic Oxygen Converter>Continuous Cast>Fully Killed Steel>SiAlK
Specification : IS 2062 E 250 BR : 2011 RA 2016

We certify that the material described below fully conforms to IS 2062 : 2011 RA 2016. Chemical composition and Mechanical properties of the product, as
tested in accordance with the scheme of testing and inspection contained in the BIS certification mark Number CM/L 0057534 are as indicated against each
Order No.
(Please refer to IS 2062 : 2011 RA 2016 for details of specification requirements)
TEST RESULTS

SECTION (NOMINAL SIZE) MECHANICAL PROPERTIES Bend M Dia

Test
THICK WIDTH LENGTH Plate No Heat No YS UTS %E %E2 CHARPY V NOTCH (L) Impact Values (J)
250 MPa 410 MPa Min23(5.6 o
mm mm mm / Pc. No. I1 I2 I3 Iavg C
Min
5SqrtS0)

16 2500 12000 2688652/1 324861 344 488 29 -- 78 68 82 76 RT OK 2.0 T

324861 341 464 27 -- -- -- -- -- -- OK 2.0 T
16 2500 12000 2688652/2 324861 -- -- -- -- -- -- -- -- -- -- --
Heat CHEMICAL COMPOSITION (LADLE ANALYSIS)
N
No C S P Mn Si Al Cu Cr Ni Mo Nb V Ti 2 B CE
% % % % % % % % % % % % % ppm % %
324861 0.15 0.017 0.028 0.80 0.17 0.020 <0.02 <0.015 <0.015 <0.015 <0.010 <0.010 <0.005 -- <0.0005 0.28
Total Pieces Page / Sales Order : 2 / 2 Total Pieces / TC : 15

The Material supplied conforms to the standard rolling and weight tolerances.,
CE calculated by formula: [C + Mn/6 + ( Cr + Mo + V )/5 + ( Ni + Cu )/15 ],
RT- Room temperature as defined in the specification,
Plate sides are in UNTRIMMED condition.,
Size of impact test specimen:10x10x55 mm(above 10mm thickness) ; 7.5x10x55 mm(upto 10mm thickness),
Note:**M = Mandrel Dia, T = Plate Thickness, Length is the rolling direction of the plate,
TC as per BSEN 10204 Type 3.1,

SHARAD KUMAR SAHU

Authorized Signatory
Authorised Signatory Research & Control Laboratory, Bhilai Steel Plant
SAIL/ CMO/ BSO
 STEEL AUTHORITY OF INDIA LIMITED Page No :D-1 of 1
BHILAI STEEL PLANT IS : 2062
RESEARCH & CONTROL LAB (MECHANICAL TESTING LAB)

TEST CERTIFICATE FOR HOT ROLLED MEDIUM AND HIGH TENSILE STRUCTURAL
STEEL
CM/L-0057534
MTL-II/QR-2

Sold-to-Party: [Link] : RCL/MTL/PLM/80641555

SHREEJEE STRUCTURAL STEEL PVT. LTD. T.C. Date : 30.04.2021
222, GIRIRAJ BUILDING , [Link], SALES ORDER NO : 1100367967
MUMBAI 400009 DA No : 80641555
Ship-to-Party:
SHREEJEE STRUCTURAL STEEL PVT. LTD.,Raigad. Wagon No / Trailer No : SER57071910417
Process of Manufacture of Steel : Basic Oxygen Converter>Continuous Cast>Fully Killed Steel>SiAlK
Specification : IS 2062 E 250 BR : 2011 RA 2016

We certify that the material described below fully conforms to IS 2062 : 2011 RA 2016. Chemical composition and Mechanical properties of the product, as
tested in accordance with the scheme of testing and inspection contained in the BIS certification mark Number CM/L 0057534 are as indicated against each
Order No.
(Please refer to IS 2062 : 2011 RA 2016 for details of specification requirements)
TEST RESULTS

SECTION (NOMINAL SIZE) MECHANICAL PROPERTIES Bend M Dia

Test
THICK WIDTH LENGTH Plate No Heat No YS UTS %E %E2 CHARPY V NOTCH (L) Impact Values (J)
240 MPa 410 MPa Min23(5.6 o
mm mm mm / Pc. No. I1 I2 I3 Iavg C
Min
5SqrtS0)

25 2500 6300 2687981/1 321817 336 463 28 -- 80 88 92 87 RT OK 2.0 T

321817 326 456 27 -- -- -- -- -- -- OK 2.0 T
25 2500 6300 2687981/2 321817 -- -- -- -- -- -- -- -- -- -- --
25 2500 6300 2687981/3 321817 -- -- -- -- -- -- -- -- -- -- --
Heat CHEMICAL COMPOSITION (LADLE ANALYSIS)
N
No C S P Mn Si Al Cu Cr Ni Mo Nb V Ti 2 B CE
% % % % % % % % % % % % % ppm % %
321817 0.15 0.020 0.028 0.78 0.17 0.022 <0.02 <0.015 <0.015 <0.015 <0.010 <0.010 <0.005 -- <0.0005 0.28
Total Pieces Page / Sales Order : 3 / 3 Total Pieces / TC : 15

The Material supplied conforms to the standard rolling and weight tolerances.,
CE calculated by formula: [C + Mn/6 + ( Cr + Mo + V )/5 + ( Ni + Cu )/15 ],
RT- Room temperature as defined in the specification,
Plate sides are in UNTRIMMED condition.,
Size of impact test specimen:10x10x55 mm(above 10mm thickness) ; 7.5x10x55 mm(upto 10mm thickness),
Note:**M = Mandrel Dia, T = Plate Thickness, Length is the rolling direction of the plate,
TC as per BSEN 10204 Type 3.1,

SHARAD KUMAR SAHU

Authorized Signatory
Authorised Signatory Research & Control Laboratory, Bhilai Steel Plant
SAIL/ CMO/ BSO
 STEEL AUTHORITY OF INDIA LIMITED Page No :E-1 of 1
BHILAI STEEL PLANT IS : 2062
RESEARCH & CONTROL LAB (MECHANICAL TESTING LAB)

TEST CERTIFICATE FOR HOT ROLLED MEDIUM AND HIGH TENSILE STRUCTURAL
STEEL
CM/L-0057534
MTL-II/QR-2

Sold-to-Party: [Link] : RCL/MTL/PLM/80641555

SHREEJEE STRUCTURAL STEEL PVT. LTD. T.C. Date : 30.04.2021
222, GIRIRAJ BUILDING , [Link], SALES ORDER NO : 1100367984
MUMBAI 400009 DA No : 80641555
Ship-to-Party:
SHREEJEE STRUCTURAL STEEL PVT. LTD.,Raigad. Wagon No / Trailer No : SER57071910417
Process of Manufacture of Steel : Basic Oxygen Converter>Continuous Cast>Fully Killed Steel>SiAlK
Specification : IS 2062 E 250 BR : 2011 RA 2016

We certify that the material described below fully conforms to IS 2062 : 2011 RA 2016. Chemical composition and Mechanical properties of the product, as
tested in accordance with the scheme of testing and inspection contained in the BIS certification mark Number CM/L 0057534 are as indicated against each
Order No.
(Please refer to IS 2062 : 2011 RA 2016 for details of specification requirements)
TEST RESULTS

SECTION (NOMINAL SIZE) MECHANICAL PROPERTIES Bend M Dia

Test
THICK WIDTH LENGTH Plate No Heat No YS UTS %E %E2 CHARPY V NOTCH (L) Impact Values (J)
250 MPa 410 MPa Min23(5.6 o
mm mm mm / Pc. No. I1 I2 I3 Iavg C
Min
5SqrtS0)

16 2000 12000 2689098/1 324912 342 475 27 -- 108 148 124 127 RT OK 2.0 T
324912 321 480 27 -- -- -- -- -- -- OK 2.0 T
Heat CHEMICAL COMPOSITION (LADLE ANALYSIS)
N
No C S P Mn Si Al Cu Cr Ni Mo Nb V Ti 2 B CE
% % % % % % % % % % % % % ppm % %
324912 0.16 0.014 0.030 0.84 0.18 0.012 <0.02 0.019 <0.015 <0.015 <0.010 <0.010 <0.005 -- <0.0005 0.30
Total Pieces Page / Sales Order : 1 / 1 Total Pieces / TC : 15

The Material supplied conforms to the standard rolling and weight tolerances.,
CE calculated by formula: [C + Mn/6 + ( Cr + Mo + V )/5 + ( Ni + Cu )/15 ],
RT- Room temperature as defined in the specification,
Plate sides are in UNTRIMMED condition.,
Size of impact test specimen:10x10x55 mm(above 10mm thickness) ; 7.5x10x55 mm(upto 10mm thickness),
Note:**M = Mandrel Dia, T = Plate Thickness, Length is the rolling direction of the plate,
TC as per BSEN 10204 Type 3.1,

SHARAD KUMAR SAHU

Authorized Signatory
Authorised Signatory Research & Control Laboratory, Bhilai Steel Plant
SAIL/ CMO/ BSO
 STEEL AUTHORITY OF INDIA LIMITED Page No :F-1 of 1
BHILAI STEEL PLANT IS : 2062
RESEARCH & CONTROL LAB (MECHANICAL TESTING LAB)

TEST CERTIFICATE FOR HOT ROLLED MEDIUM AND HIGH TENSILE STRUCTURAL
STEEL
CM/L-0057534
MTL-II/QR-2

Sold-to-Party: [Link] : RCL/MTL/PLM/80641555

SHREEJEE STRUCTURAL STEEL PVT. LTD. T.C. Date : 30.04.2021
222, GIRIRAJ BUILDING , [Link], SALES ORDER NO : 1100367986
MUMBAI 400009 DA No : 80641555
Ship-to-Party:
SHREEJEE STRUCTURAL STEEL PVT. LTD.,Raigad. Wagon No / Trailer No : SER57071910417
Process of Manufacture of Steel : Basic Oxygen Converter>Continuous Cast>Fully Killed Steel>SiAlK
Specification : IS 2062 E 250 BR : 2011 RA 2016

We certify that the material described below fully conforms to IS 2062 : 2011 RA 2016. Chemical composition and Mechanical properties of the product, as
tested in accordance with the scheme of testing and inspection contained in the BIS certification mark Number CM/L 0057534 are as indicated against each
Order No.
(Please refer to IS 2062 : 2011 RA 2016 for details of specification requirements)
TEST RESULTS

SECTION (NOMINAL SIZE) MECHANICAL PROPERTIES Bend M Dia

Test
THICK WIDTH LENGTH Plate No Heat No YS UTS %E %E2 CHARPY V NOTCH (L) Impact Values (J)
250 MPa 410 MPa Min23(5.6 o
mm mm mm / Pc. No. I1 I2 I3 Iavg C
Min
5SqrtS0)

20 2000 12000 2689127/1 315877 267 435 31 -- -- -- -- -- RT OK 2.0 T

315877 346 488 30 -- 62 66 68 65 RT OK 2.0 T
Heat CHEMICAL COMPOSITION (LADLE ANALYSIS)
N
No C S P Mn Si Al Cu Cr Ni Mo Nb V Ti 2 B CE
% % % % % % % % % % % % % ppm % %
315877 0.16 0.015 0.021 0.87 0.26 0.028 <0.02 <0.015 <0.015 <0.015 <0.010 <0.010 <0.005 -- <0.0005 0.31
Total Pieces Page / Sales Order : 1 / 1 Total Pieces / TC : 15

The Material supplied conforms to the standard rolling and weight tolerances.,
CE calculated by formula: [C + Mn/6 + ( Cr + Mo + V )/5 + ( Ni + Cu )/15 ],
RT- Room temperature as defined in the specification,
Plate sides are in UNTRIMMED condition.,
Size of impact test specimen:10x10x55 mm(above 10mm thickness) ; 7.5x10x55 mm(upto 10mm thickness),
Note:**M = Mandrel Dia, T = Plate Thickness, Length is the rolling direction of the plate,
TC as per BSEN 10204 Type 3.1,

SHARAD KUMAR SAHU

Authorized Signatory
Authorised Signatory Research & Control Laboratory, Bhilai Steel Plant
SAIL/ CMO/ BSO
 STEEL AUTHORITY OF INDIA LIMITED Page No :G-1 of 1
BHILAI STEEL PLANT IS : 2062
RESEARCH & CONTROL LAB (MECHANICAL TESTING LAB)

TEST CERTIFICATE FOR HOT ROLLED MEDIUM AND HIGH TENSILE STRUCTURAL
STEEL
CM/L-0057534
MTL-II/QR-2

Sold-to-Party: [Link] : RCL/MTL/PLM/80641555

SHREEJEE STRUCTURAL STEEL PVT. LTD. T.C. Date : 30.04.2021
222, GIRIRAJ BUILDING , [Link], SALES ORDER NO : 1100368004
MUMBAI 400009 DA No : 80641555
Ship-to-Party:
SHREEJEE STRUCTURAL STEEL PVT. LTD.,Raigad. Wagon No / Trailer No : SER57071910417
Process of Manufacture of Steel : Basic Oxygen Converter>Continuous Cast>Fully Killed Steel>SiAlK
Specification : IS 2062 E 250 BR : 2011 RA 2016

We certify that the material described below fully conforms to IS 2062 : 2011 RA 2016. Chemical composition and Mechanical properties of the product, as
tested in accordance with the scheme of testing and inspection contained in the BIS certification mark Number CM/L 0057534 are as indicated against each
Order No.
(Please refer to IS 2062 : 2011 RA 2016 for details of specification requirements)
TEST RESULTS

SECTION (NOMINAL SIZE) MECHANICAL PROPERTIES Bend M Dia

Test
THICK WIDTH LENGTH Plate No Heat No YS UTS %E %E2 CHARPY V NOTCH (L) Impact Values (J)
240 MPa 410 MPa Min23(5.6 o
mm mm mm / Pc. No. I1 I2 I3 Iavg C
Min
5SqrtS0)

40 1600 12000 2688774/1 324888 325 479 26 -- 128 144 106 126 RT OK 3.0 T
324888 328 475 26 -- -- -- -- -- -- OK 3.0 T
40 1600 12000 2688776/1 324888 -- -- -- -- -- -- -- -- -- -- --
Heat CHEMICAL COMPOSITION (LADLE ANALYSIS)
N
No C S P Mn Si Al Cu Cr Ni Mo Nb V Ti 2 B CE
% % % % % % % % % % % % % ppm % %
324888 0.17 0.009 0.020 0.87 0.17 0.012 <0.02 <0.015 <0.015 <0.015 <0.010 <0.010 <0.005 -- <0.0005 0.32
Total Pieces Page / Sales Order : 2 / 2 Total Pieces / TC : 15

The Material supplied conforms to the standard rolling and weight tolerances.,
CE calculated by formula: [C + Mn/6 + ( Cr + Mo + V )/5 + ( Ni + Cu )/15 ],
RT- Room temperature as defined in the specification,
Plate sides are in UNTRIMMED condition.,
Size of impact test specimen:10x10x55 mm(above 10mm thickness) ; 7.5x10x55 mm(upto 10mm thickness),
Note:**M = Mandrel Dia, T = Plate Thickness, Length is the rolling direction of the plate,
TC as per BSEN 10204 Type 3.1,

SHARAD KUMAR SAHU

Authorized Signatory
Authorised Signatory Research & Control Laboratory, Bhilai Steel Plant
SAIL/ CMO/ BSO