ASTM-C127!88!1993 - Specific Gravity Coarse Aggregates

TS-1c T 85-1 AASHTO
Standard Method of Test for

Specific Gravity and Absorption
of Coarse Aggregate
AASHTO Designation: T 85-91 (2004)
1

ASTM Designation: C 127-88 (1993)
1. SCOPE
1.1. This method covers the determination of specific gravity and absorption of coarse aggregate.
The specific gravity may be expressed as bulk specific gravity, bulk specific gravity (saturated-
surface-dry (SSD)), or apparent specific gravity. The bulk specific gravity (SSD) and absorption
are based on aggregate after 15 hours soaking in water. This method is not intended to be used
with lightweight aggregates.
1.2. The values stated in SI units are to be regarded as the standard.
1.3. This standard may involve hazardous materials, operations, and equipment. This standard does
not purport to address all of the safety problems associated with its use. It is the responsibility of
the user of this standard to consult and establish appropriate safety and health practices and
determine the applicability of regulatory limitations prior to use.
2. REFERENCED DOCUMENTS
2.1. AASHTO Standards:
M 43, Sizes of Aggregate for Road and Bridge Construction
M 92, Wire-Cloth Sieves for Testing Purposes
M 132, Terms Relating to Density and Specific Gravity of Solids, Liquids, and Gases
M 231, Weighing Devices Used in the Testing of Materials
R 1, Use of the International System of Units
T 2, Sampling of Aggregates
T 19M/T 19, Bulk Density (Unit Weight) and Voids in Aggregate
T 27, Sieve Analysis of Fine and Coarse Aggregates
T 84, Specific Gravity and Absorption of Fine Aggregate
T 248, Reducing Samples of Aggregate to Testing Size
T 255, Total Evaporable Moisture Content of Aggregate by Drying
2.2. ASTM Standards:
C 125, Terminology Relating to Concrete and Concrete Aggregates
C 670, Practice of Preparing Precision Statements for Test Methods for Construction
Materials
Copyright American Association of State Highway and Transportation Officials
Provided by IHS under license with AASHTO Licensee=Purdue University/5923082001
Not for Resale, 09/12/2007 08:50:38 MDT No reproduction or networking permitted without license from IHS
-
-
`
,
`
,
,
`
`
`
,
,
`
,
,
,
,
`
`
`
,
`
`
,
`
`
`
,
`
,
-
`
-
`
,
,
`
,
,
`
,
`
,
,
`
-
-
-
TS-1c T 85-2 AASHTO
3. TERMINOLOGY
3.1. Definitions:
3.1.1. absorptionthe increase in the mass of aggregate due to water in the pores of the material, but not
including water adhering to the outside surface of the particles, expressed as a percentage of the
dry mass. The aggregate is considered dry when it has been maintained at a temperature of 110
5C for sufficient time to remove all uncombined water.
3.1.2. specific gravitythe ratio of the mass (or weight in air) of a unit volume of a material to the mass
of the same volume of water at stated temperatures. Values are dimensionless.
3.1.2.1. apparent specific gravitythe ratio of the weight in air of a unit volume of the impermeable
portion of aggregate at a stated temperature to the weight in air of an equal volume of gas-free
distilled water at a stated temperature.
3.1.2.2. bulk specific gravitythe ratio of the weight in air of a unit volume of aggregate (including
the permeable and impermeable voids in the particles, but not including the voids between
particles) at a stated temperature to the weight in air of an equal volume of gas-free distilled water
at a stated temperature.
3.1.2.3. bulk specific gravity (SSD)the ratio of the mass in air of a unit volume of aggregate,
including the mass of water within the voids filled to the extent achieved by submerging in
water for approximately 15 hours (but not including the voids between particles) at a stated
temperature, compared to the weight in air of an equal volume of gas-free distilled water at a
stated temperature.
4. SUMMARY OF METHOD
4.1. A sample of aggregate is immersed in water for approximately 15 hours to essentially fill the
pores. It is then removed from the water, the water dried from the surface of the particles, and
weighed. Subsequently the sample is weighed while submerged in water. Finally the sample is
oven-dried and weighed a third time. Using the mass and weight measurements thus obtained and
formulas in the method, it is possible to calculate three types of specific gravity and absorption.
5. SIGNIFICANCE AND USE
5.1. Bulk specific gravity is the characteristic generally used for calculation of the volume occupied by
the aggregate in various mixtures containing aggregate, including portland cement concrete,
bituminous concrete, and other mixtures that are proportioned or analyzed on an absolute volume
basis. Bulk specific gravity is also used in the computation of voids in aggregate in T 19M/T 19.
Bulk specific gravity (SSD) is used if the aggregate is wet, that is, if its absorption has been
satisfied. Conversely, the bulk specific gravity (oven-dry) is used for computations when the
aggregate is dry or assumed to be dry.
5.2. Apparent specific gravity pertains to the relative density of the solid material making up the
constituent particles not including the pore space within the particles which is accessible to water.
-
-
`
,
`
,
,
`
`
`
,
,
`
,
,
,
,
`
`
`
,
`
`
,
`
`
`
,
`
,
-
`
-
`
,
,
`
,
,
`
,
`
,
,
`
-
-
-
TS-1c T 85-3 AASHTO
5.3. Absorption values are used to calculate the change in the mass of an aggregate due to water
absorbed in the pore spaces within the constituent particles, compared to the dry condition, when it
is deemed that the aggregate has been in contact with water long enough to satisfy most of the
absorption potential. The laboratory standard for absorption is that obtained after submerging dry
aggregate for approximately 15 hours in water. Aggregates mined from below the water table may
have a higher absorption, when used, if not allowed to dry. Conversely, some aggregates when
used may contain an amount of absorbed moisture less than the 15-hour soaked condition. For an
aggregate that has been in contact with water and that has free moisture on the particle surfaces,
the percentage of free moisture can be determined by deducting the absorption from the total
moisture content determined by T 255.
5.4. The general procedures described in this method are suitable for determining the absorption of
aggregates that have had conditioning other than the 15-hour soak, such as boiling water or
vacuum saturation. The values obtained for absorption by other methods will be different than the
values obtained by the prescribed 15-hour soak, as will the bulk specific gravity (SSD).
5.5. The pores in lightweight aggregates may or may not become essentially filled with water after
immersion for 15 hours. In fact, many such aggregates can remain immersed in water for several
days without satisfying most of the aggregates absorption potential. Therefore, this method is not
intended for use with lightweight aggregate.
Note 1The terminology for specific gravity is based on terms in M 132, and that for absorption
is based on that term in ASTM C 125.
6. APPARATUS
6.1. Balance, conforming to the requirements of M 231, Class G 5. The balance shall be equipped with
suitable apparatus for suspending the sample container in water from the center of the weighing
platform or pan of the balance.
6.2. Sample ContainerA wire basket of 3.35 mm (No. 6) or finer mesh, or a bucket of approximately
equal breadth and height, with a capacity of 4 to 7 L for 37.5-mm (1
1
/
2
-in.) nominal maximum size
aggregate or smaller, and a larger container as needed for testing larger maximum size aggregate.
The container shall be constructed so as to prevent trapping air when the container is submerged.
6.3. Water TankA watertight tank into which the sample and container are placed for complete
immersion while suspended below the balance, equipped with an overflow outlet for maintaining a
constant water level.
6.4. Suspended ApparatusWire suspending the container shall be of the smallest practical size to
minimize any possible effects of a variable immersed length.
6.5. SievesA 4.75-mm (No. 4) sieve or other sizes as needed (Sections 7.2, 7.3, and 7.4), conforming
to M 92.
-
-
`
,
`
,
,
`
`
`
,
,
`
,
,
,
,
`
`
`
,
`
`
,
`
`
`
,
`
,
-
`
-
`
,
,
`
,
,
`
,
`
,
,
`
-
-
-
TS-1c T 85-4 AASHTO
7. SAMPLING
7.1. Sample the aggregate in accordance with T 2.
7.2. Thoroughly mix the sample of aggregate and reduce it to the approximate quantity needed using
the applicable procedures in T 248. Reject all material passing a 4.75-mm (No. 4) sieve by dry
sieving and thoroughly washing to remove dust or other coatings from the surface. If the coarse
aggregate contains a substantial quantity of material finer than the 4.75-mm (No. 4) sieve (such as
for Size No. 8 and 9 aggregates in M 43), use the 2.36-mm (No. 8) sieve in place of the 4.75-mm
(No. 4) sieve. Alternatively, separate the material finer than the 4.75-mm (No. 4) sieve and test the
finer material according to T 84.
7.3. The minimum mass of test sample to be used is given below. In many instances it may be
desirable to test a coarse aggregate in several separate size fractions; and if the sample contains
more than 15 percent retained on the 37.5-mm (1
1
/
2
-in.) sieve, test the material larger than
37.5 mm in one or more size fractions separately from the smaller size fractions. When an
aggregate is tested in separate size fractions, the minimum mass of test sample for each fraction
shall be the difference between the masses prescribed for the maximum and minimum sizes of
the fraction.
Nominal Maximum
Size, mm (in.)
Minimum Mass of
Test Sample, kg (lb)
12.5 (
1
/
2
) or less 2 (4.4)
19.0 (
3
/
4
) 3 (6.6)
25.0 (1) 4 (8.8)
37.5 (1
1
/
2
) 5 (11)
50 (2) 8 (18)
63 (2
1
/
2
) 12 (26)
75 (3) 18 (40)
90 (3
1
/
2
) 25 (55)
100 (4) 40 (88)
112 (4
1
/
2
) 50 (110)
125 (5) 75 (165)
150 (6) 125 (276)

7.4. If the sample is tested in two or more size fractions, determine the grading of the sample in
accordance with T 27, including the sieves used for separating the size fractions for the
determinations in this method. In calculating the percentage of material in each size fraction,
ignore the quantity of material finer than the 4.75-mm (No. 4) sieve or 2.36-mm (No. 8) sieve
when that sieve is used in accordance with Section 7.2.
8. PROCEDURE
8.1. Dry the test sample to constant mass at a temperature of 110 5C (230 9F), cool in air at room
temperature for one to three hours for test samples of 37.5 mm (1
1
/
2
-in.) nominal maximum size,
or longer for larger sizes until the aggregate has cooled to a temperature that is comfortable to
handle (approximately 50C). Subsequently immerse the aggregate in water at room temperature
for a period of 15 to 19 hours.
Note 2When testing coarse aggregate of large nominal maximum size requiring large test
samples, it may be more convenient to perform the test on two or more subsamples, and the values
obtained combined for the computation described in Section 9.
-
-
`
,
`
,
,
`
`
`
,
,
`
,
,
,
,
`
`
`
,
`
`
,
`
`
`
,
`
,
-
`
-
`
,
,
`
,
,
`
,
`
,
,
`
-
-
-
TS-1c T 85-5 AASHTO
8.2. Where the absorption and specific gravity values are to be used in proportioning concrete mixtures
in which the aggregates will be in their naturally moist condition, the requirement for initial drying
to constant mass may be eliminated, and, if the surfaces of the particles in the sample have been
kept continuously wet until test, the 15-hour soaking may also be eliminated.
Note 3Values for absorption and bulk specific gravity (SSD) may be significantly higher for
aggregate not oven dried before soaking than for the same aggregate treated in accordance with
Section 8.1. This is especially true of particles larger than 75 mm (3 in.) since the water may not
be able to penetrate the pores to the center of the particle in the prescribed soaking period.
8.3. Remove the test sample from the water and roll it in a large absorbent cloth until all visible films
of water are removed. Wipe the larger particles individually. A moving stream of air may be used
to assist in the drying operation. Take care to avoid evaporation of water from aggregate pores
during the operation of surface-drying. Determine the mass of the test sample in the saturated
surface-dry condition. Record this and all subsequent masses to the nearest 1.0 g or 0.1 percent of
the sample mass, whichever is greater.
8.4. After determining the mass, immediately place the saturated-surface-dry test sample in the
sample container and determine its mass in water at 23.0 1.7C (73.4 3F), having a density
of 997 2 kg/m
3
. Take care to remove all entrapped air before determining the mass by shaking
the container while immersed.
Note 4The container should be immersed to a depth sufficient to cover it and the test sample
during mass determination. Wire suspending the container should be of the smallest practical size
to minimize any possible effects of a variable immersed length.
8.5. Dry the test sample to constant mass at a temperature of 110 5C (230 9F), cool in air at room
temperature one to three hours, or until the aggregate has cooled to a temperature that is
comfortable to handle (approximately 50C), and determine the mass. Use this weight for A in the
calculations in Section 9.
9. CALCULATIONS
9.1. Specific Gravity:
9.1.1. Bulk Specific GravityCalculate the bulk specific gravity, 23/23C (73.4/73.4F), as follows:
( ) C B A = gr sp Bulk (1)
where:
A = mass of oven-dry test sample in air, g;
B = mass of saturated-surface-dry test sample in air, g; and
C = mass of saturated test sample in water, g.
9.1.2. Bulk Specific Gravity (Saturated-Surface-Dry)Calculate the bulk specific gravity, 23/23C
(73.4/73.4F), on the basis of mass of saturated-surface-dry aggregate as follows:
( ) ( ) C B B = dry - surface - saturated gr sp Bulk (2)
9.1.3. Apparent Specific GravityCalculate the apparent specific gravity, 23/23C (73.4/73.4F),
as follows:
( ) C A A = gr sp Apparent (3)
-
-
`
,
`
,
,
`
`
`
,
,
`
,
,
,
,
`
`
`
,
`
`
,
`
`
`
,
`
,
-
`
-
`
,
,
`
,
,
`
,
`
,
,
`
-
-
-
TS-1c T 85-6 AASHTO
9.2. Average Specific Gravity ValuesWhen the sample is tested in separate size fractions, the
average value for bulk specific gravity, bulk specific gravity (SSD), or apparent specific gravity
can be computed as the weighted average of the values as computed in accordance with Section
9.1 using the following equation:
n
n
G
P
G
P
G
P
G
100 100 100
1
2
2
1
1
+ +
= (4)
where:
G = average specific gravity (All forms of expression of specific gravity can be
averaged in this manner.);
G
1
, G
2
G
n
= appropriate specific gravity values for each size fraction depending on the type
of specific gravity being averaged; and
P
1
, P
2
P
n
= mass percentages of each size fraction present in the original sample.
Note 5Some users of this method may wish to express the results in terms of density. Density
may be determined by multiplying the bulk specific gravity, bulk specific gravity (SSD), or
apparent specific gravity by the density of water (997.5 kg/m
3
or 0.9975 Mg/m
3
or 62.27 lb/ft
3
at
23C). Some authorities recommend using the density of water at 4C (1000 kg/m
3
or 1.000
Mg/m
3
or 62.43 lb/ft
3
) as being sufficiently accurate. Results should be expressed to three
significant figures. The density terminology corresponding to bulk specific gravity, bulk specific
gravity (SSD), and apparent specific gravity has not been standardized.
9.3. AbsorptionCalculate the percentage of absorption, as follows:
( ) [ ] 100 percent , Absorption = A A B (5)
9.4. Average Absorption ValueWhen the sample is tested in separate size fractions, the average
absorption value is the average of the values as computed in Section 9.3, weighted in proportion to
the mass percentages of the size fractions in the original sample as follows:
( ) ( ) ( ) 100 100 100
2 2 1 1 n n
A P A P A P A + + = (6)
where:
A = average absorption, percent;
A
1
, A
2
A
n
= absorption percentages for each size fraction; and
P
1
, P
2
P
n
= mass percentages of each size fraction present in the original sample.
10. REPORT
10.1. Report specific gravity results to the nearest 0.01, and indicate the type of specific gravity,
whether bulk, bulk (saturated-surface-dry), or apparent.
10.2. Report the absorption result to the nearest 0.1 percent.
10.3. If the specific gravity and absorption values were determined without first drying the aggregate, as
permitted in Section 8.2, it shall be noted in the report.
-
-
`
,
`
,
,
`
`
`
,
,
`
,
,
,
,
`
`
`
,
`
`
,
`
`
`
,
`
,
-
`
-
`
,
,
`
,
,
`
,
`
,
,
`
-
-
-
TS-1c T 85-7 AASHTO
11. PRECISION AND BIAS
11.1. The estimates of precision of this test method listed in Table 1 are based on results from the
AASHTO Materials Reference Laboratory Reference Sample Program, with testing conducted
by this test method and ASTM C 127. The significant difference between the methods is that
ASTM C 127 requires a saturation period of 24 4 hours, while T 85 requires a saturation
period of 15 hours minimum. This difference has been found to have insignificant effect on the
precision indices. The data are based on the analyses of more than 100 paired test results from
40 to 100 laboratories.
Table 1Precision

Standard
Deviation
(1S)
a

Acceptable
Range of
Two Results
(D2S)
a

Single-operator precision:
Bulk specific gravity (dry) 0.009 0.025
Bulk specific gravity (SSD) 0.007 0.020
Apparent specific gravity 0.007 0.020
Absorption,
b
percent 0.088 0.25

Multilaboratory precision:
Bulk specific gravity (dry) 0.013 0.038
Bulk specific gravity (SSD) 0.011 0.032
Apparent specific gravity 0.011 0.032
Absorption,
b
percent 0.145 0.41
a
These numbers represent, respectively, the (1S) and (D2S) limits as described in ASTM C 670. The
precision estimates were obtained from the analysis of combined AASHTO Materials Reference
Laboratory reference sample data from laboratories using 15-hour minimum saturation times and
other laboratories using 24 4-hour saturation time. Testing was performed on aggregates of normal
specific gravities and started with aggregates in the oven-dry condition.
b
Precision estimates are based on aggregates with absorptions of less than 2 percent.

11.2. BiasSince there is no accepted reference material for determining the bias for the procedure in
this test method, no statement on bias is being made.
--`,`,,```,,`,,,,```,``,```,`,-`-`,,`,,`,`,,`---
TS-1c T 85-8 AASHTO
APPENDICES
(Nonmandatory Information)
A1. DEVELOPMENT OF EQUATIONS
A1.1. The derivation of the equation is apparent from the following simplified cases using two solids.
Solid 1 has a mass W
1
in grams and a volume V
1
in milliliters; its specific gravity (G
1
) is therefore
W
1
/V
1
. Solid 2 has a mass W
2
and volume V
2
, and G
2
= W
2
/V
2
. If the two solids are considered
together, the specific gravity of the combination is the total mass in grams divided by the total
volume in milliliters:
) /( ) (
2 1 2 1
V V W W G + + = (7)
Manipulation of this equation yields the following:
2 1
2
2 1
1
2 1
2 1
1 1
W W
V
W W
V
W W
V V
G
+
+
+
=
+
+
= (8)
+
+
+
=
2
2
2 1
2
1
1
2 1
1
1
W
V
W W
W
W
V
W W
W
G (9)
However, the mass fractions of the two solids are:
( ) 100
1 2 1 1
P W W W = + (10)
and:
( ) 100
2 2 1 2
P W W W = + (11)
and:
2 2 2 1 1 1
1 and 1 W V G W V G = = (12)
therefore:
( )( ) ( )( ) [ ]
2 2 1 1
1 100 1 100 1 G P G P G + = (13)
An example of the computation is given in Table 2.
Table 2Example Calculation of Average Values of Specific Gravity and Absorption for a Course Aggregate
Tested in Separate Sizes
Size Fraction,
mm (in.)
Percent in
Original Sample
Bulk Specific
Gravity (SSD)
a

Sample Mass
Used in Test, g
Absorption,
percent
4.75 to 12.5 44 27.2 2213.0 0.4
(No. 4 to
1
/
2
)
12.5 to 37.5 35 2.56 5462.5 2.5
(
1
/
2
to 1
1
/
2
)
37.5 to 63 21 2.54 12593.0 3.0
(1
1
/
2
to 2
1
/
2
)
a
Average Specific Gravity (SSD)

1
2.62
0.44 0.35 0.21
2.72 2.56 2.54
SSD
G = =
+ +
(14)
Average Absorption:
( ) ( ) ( ) ( ) ( ) ( ) 0.44 0.4 0.35 2.5 0.21 3.0 1.7% A = + + = (15)
-
-
`
,
`
,
,
`
`
`
,
,
`
,
,
,
,
`
`
`
,
`
`
,
`
`
`
,
`
,
-
`
-
`
,
,
`
,
,
`
,
`
,
,
`
-
-
-
TS-1c T 85-9 AASHTO
A2. INTERRELATIONSHIPS BETWEEN SPECIFIC GRAVITIES AND
ABSORPTION AS DEFINED IN METHODS T 85 AND T 84
A2.1. Let:
S
d
= bulk specific gravity (dry basis),
S
s
= bulk specific gravity (SSD basis),
S
a
= apparent specific gravity, and
A = absorption in percent.
A2.2. Then:
( )
d s
S A S 100 1+ = (16)
1
1
1
100
100
S
d
S
a
A AS
d
S
d
= =

(17)
1
1 100
100
S
d
A A
S
s
=
+
(18)

( ) 1 1
100
S
s
A
S
s
=

100 1
=
d
s
S
S
A (19)

( )
100
1

=
s a
s a
S S
S S
A (20)

1
This method agrees with ASTM C 127-88 except for differences in soaking time, accuracy of weighing, balance
requirements, water tank requirements and SI units.
-
-
`
,
`
,
,
`
`
`
,
,
`
,
,
,
,
`
`
`
,
`
`
,
`
`
`
,
`
,
-
`
-
`
,
,
`
,
,
`
,
`
,
,
`
-
-
-

ASTM-C127!88!1993 - Specific Gravity Coarse Aggregates

Uploaded by

ASTM-C127!88!1993 - Specific Gravity Coarse Aggregates

Uploaded by

TS-1c T 85-1 AASHTO

Standard Method of Test for

You might also like