Polycoat RBE 1000

SBS modified bitumen jellified emulsion

Emulsified bituminous waterproofing and protective coating with high SBS rubber

DUBAI GREEN BUILDING REGULATIONS

Certificate No. CL17020460

characteristics
► Cold applied.
► Single component, easy to apply.
► Can be applied on damp substrates.
► Asbestos free, odorless. Can be applied in closed or
confined spaces.

TDS_Polycoat RBE 1000_GCC_0519

► Solvent free & environmentally friendly.
► Good resistance against chloride and sulphate ions.
► Has good adhesion to most building substrates.
► Seamless/joint free.

waterproofing

DESCRIPTION 1
Polycoat RBE 1000 is an emulsified bituminous coating
modified with high content of Styrene Butadiene Styrene
rubber, which dries to form a tough and seamless, flexible be applied to damp or freshly cast concrete surfaces also.
water and vapor proof protective coating. However, it should not be applied on waterlogged or
flowing water areas. In case of delay in application of the
application instructions top coat for more than 24 hours, a fresh coat of primer
Application procedures may vary slightly depending upon shall be re-applied.
site conditions. the general recommended guideline for the Foundation Waterproofing
application of the bitumen coating system is as follows: Stir the contents of the drum thoroughly before application
Surface preparation to remove all sediments. Depending on the dry film
The surface shall be cleaned thoroughly of all contaminants thickness required, apply the jellified emulsion @1–2m²/L/
like dust, traces of curing compound, oil, grease. Light coat at required no. coats. 2nd coat or Subsequent coats
mechanical grinding/grit blasting/high pressure water jet shall be applied only after the previous coat dries off
may be used to clean the surface of all the contaminants completely and shall be applied at right angles to the
depending on the degree of contamination on the surface previous coat. Clean dry sand may be broadcasted onto
to be coated. All surface imperfections and protrusions the wet coating to provide a key for the subsequent coats
shall be removed and repaired. Structurally unsound and and achieve a greater dry film thickness. If a plaster or
friable concrete must be removed and repaired with a cement render is to be applied on the bitumen coated
suitable Polycrete* concrete repair mortar. surface, broadcast clean, dry sand over the primer caoting
whilst it is in wet condition. Care shall be taken to ensure
Priming that the first coat is not punctured during the application
It is highly recommended to apply a priming coat prior of the second coat. However, if the coating is damaged,
to the application of the Polycoat RBE 1000 coating on the area can be readily over coated provided the surface
the substrate. The primer can be prepared in the site by preparation is done properly.
diluting Polycoat RBE 1000 with 20% water and applying
this diluted coat as the primer. For very dry and porous Protection
substrates apply two coats of this primer. The primer can Polycoat RBE 1000 coating should be protected from
 getting damaged due to the ongoing site activities. TECHNICAL PROPERTIES
coating can be protected either by a cement sand
PROPERTIES VALUES TEST STANDARDS
screed (50mm thick) or by an asphaltic protection board
(Bituboard*). Alternatively, a 1000 gauge polythene sheet Color Dark brown -
can also be used for protecting the coating in areas where Form Thixotropic
the backfill material is not very coarse. viscous liquid -
COVERAGE Density @25°C,
[g/cc] 1.05±0.05 ASTM D 1475
The coating shall be applied at a coverage rate of 1-2m2/
L/coat at required no. of coats and may vary depending on Solid content,
the requirement. [%by wt] >65 ASTM D 2939
Tensile strength,
CLEANING [N/mm2] >0.2 ASTM D 412
Clean all tools immediately after use with clean water. Elongation, [%] >1000 ASTM D 412
Hardened material can be cleaned with a suitable cleaner.
Rubber content, [%] >15 on the
STORAGE & SHELF LIFE dried film ASTM D 1644
The pails and drums must be stored in a covered Recovery, [%] 100 ASTM D 412
area, away from direct sunlight, UV and other sources Peel adhesion
of heat. The shelf life of the product is up to 12 strength [N/mm] >4 ASTM D 903
months in un-opened condition and when stored as Heat resistance
per recommendations. Failure to comply with the @100°C no flow ASTM D 2939
recommended storage conditions and excessive exposure
TDS_Polycoat RBE 1000_GCC_0519

Low temperature
to sunlight and UV will result in the deterioration of the
flexibility, [°C] ≤ -10 ASTM D 5147
quality of the product and reduce its shelf life.
Water vapor ASTM E 96
HEALTH & SAFETY transmission, <0.2
As with all bitumen products caution should always be [g/m2/24 hours]
exercised. Protective clothing such as gloves and goggles Drying time
should be worn. (See packing for specific instructions). @25°C, [min] 60 -
Treat any splashes to the skin or eyes with fresh water Application
immediately. Should any of the products be accidentally temperature [°C] 5 to 55 DIN EN 52123
swallowed, do not induce vomiting. Call for medical help
2 immediately. Ensure that the container is available for Service
medical attendant to examine any relevant instructions and temperature [°C] -5 to 100 -
content details. VOC [g/l] <50 ASTM D 3960/
D 2369
SUPPLY All values given are subject to 5-10% tolerance
Polycoat RBE 1000 200L drums
Apart from the information given here it is also important to observe the relevant
Bituboard 3.2mm 2m x 1m, wt 7.7kg guidelines and regulations of various organisations and trade associations as
6.0mm 2m x1 m, wt 14.0kg well as the respective standards. The aforementioned characteristics are based
on practical experience and applied testing. Warranted properties and possible
Watertite TS 15 10m x 50mm, wt 0.60kg uses which go beyond those warranted in this information sheet require our
# Approximate weight written confirmation. All data given was obtained at an ambient and material
temperature of +23°C and 50 % relative air humidity at laboratory conditions
unless specified otherwise. Please note that under other climatic conditions
hardening can be accelerated or delayed.
The information contained herein, particularly recommendations for the
handling and use of our products, is based on our professional experience.
As materials and conditions may vary with each intended application, and
thus are beyond our sphere of influence, we strongly recommend that in each
case sufficient tests are conducted to check the suitability of our products
for their intended use. Legal liability cannot be accepted on the basis of the
contents of this data sheet or any verbal advice given, unless there is a case
of wilful misconduct or gross negligence on our part. This technical data sheet
supersedes all previous editions relevant to this product.

Henkel Polybit Industries Ltd.; PO Box: 293, Umm Al Quwain, UAE

Tel:+971(6)76 70 777; Fax:+971(6)76 70 197; henkelpolybit@henkel.com
Henkel Polybit Industries Ltd.; PO Box: 5911, Dammam-31432, KSA
Tel:+96613808 4061 / 62, Fax: +966 13 812 1164; polybitdammam@henkel.com
www.henkelpolybit.com