Metal-receptive layer

OPP core
PP heat sealable layer

TATRAFAN ® KXNE
COEXTRUDED BOPP FILM FOR METALLIZATION

Description and Application

* Excellent metal adhesion on the treated surface, non-treated surface provides good heat-sealable
* Suitable for lamination
* Wrapping of various food products, confectioneries, meat products, textiles, etc.
* Excellent optical properties (gloss, haze) and slip properties
* Improved barrier properties (moisture, odor) and antiblocking properties

TECHNICAL DATA
PROPERTIES TEST METHOD UNITS TATRAFAN® KXNE
Thickness µm 15 20 25 30 35 40
DIN 53370
tolerance % ±5
Square weight g/m2 13,6 18,2 22,8 27,3 31,9 36,4
Internal method
tolerance % ±5
Yield Internal method m2/kg 68,5 54,9 43,9 36,6 31,3 27,5
Tensile strength

MD (min.) ISO 527-3 MPa 130

TD (min.) 250
Elongation

MD (max.) ISO 527-3 % 200

TD (max.) 65
Water vapour permeability D I N 53 122/2
g/(m2.24 h) 1,8 1,5 1,2 1,0 0,9 0,8
(max.) 2 3 ° C , 85%RV
Oxygen permeability DIN 53 380 cm3/(m2.24 h. 0,1MPa) 2300 2200 1800 1500 1300 1100
(max.)
Coefficient of friction ASTM D 1894 0,3
- film/film, Kinetic on non treatment side
Seal strength (min.) 120°C, 1s, 0,3 MPa N/15 mm film strip 2,0
Gloss ASTM D 2457 % min. 85 **
Haze ASTM D 1003 % max. 3,0 **
Surface tension STN ISO 8296 mN/m ≥ 38
* After production
** After storage
*** Typical values

www.terichem.sk
TATRAFAN ® KXNE
COEXTRUDED BOPP FILM FOR METALLIZATION

HANDLING AND STORAGE

The product does not present special safety requirements during handling and storage. In order to maintain their
properties and to ensure good processability, the film should be stored avoiding high humidity and high temperature
conditions. Do not exceed an ambient temperature of 40°C (transport temperature between (-20 + 30)°C) and rela-
tive humidity of 80%. The product should be protect away from direct sunlight and heat (steam lines or other).
Take measures against electrostatic discharges - the film will accumulate electrostatic charge of the web - it could
by cause an electrical spark (ignition source). Keep away from source of ignition.
Use with adequate ventilation.

General notes:

Do not handle or store near an open flame, sources of the heat or ignition. Store in a cool, dry area, away from direct
heat or sunlight (foil for food packaging applications keep away from hazardous chemicals).
Polypropylene films characteristics are maintained for 6 months from date of production (except for metallized layer
surface tension).

AVAILABILITY
Bobbin
Core diameter Outside diameter
(mm) (mm)
KXNE 15
KXNE 20 76 (76,8) *
KXNE 25 max. 800
KXNE 30 120 *
KXNE 35 152 *
KXNE 40
Other parameters available on request. * Standard

ENVIRONMENT
When disposed of under orderly conditions no environmental damage effects occur. During burning under free air
conditions only CO2, CO and water arise. Does not contain additives based on heavy metals (Cd, Pb, Hg, Cr). This
product is expected to persist.

OTHER INFORMATION
This information and recommendations is based on Terichem‘s best knowledge and belief accurate and reliable as
of the date indicated.
However, no representation, warranty or
guarantee is made with regards to accura-
cy, reliability or completeness. Conditions
of use of the material are under the control

TERICHEM a.s.

Štúrova 101
059 21 Svit
Slovakia

tel.: + 421 52 715 3285

fax: + 421 52 715 2303
mail: sales@terichem.sk

www.terichem.sk