Designation: B88M − 13

Standard Specification for

Seamless Copper Water Tube (Metric)1
This standard is issued under the fixed designation B88M; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.

1. Scope* 1.5 The values stated in SI units are to be regarded as

1.1 This specification covers seamless copper water tube standard. No other units of measurement are included in this
suitable for general plumbing, similar applications for the standard.
NOTE 3—This specification is the SI companion to Specification B88.
conveyance of fluids, and commonly used with solder, flared,
or compression-type fittings. The type of copper water tube 1.6 The following safety hazards caveat pertains only to the
suitable for any particular application is determined by the test methods portion, Section 15, of this specification: This
internal or external fluid pressure, by the installation and standard does not purport to address all of the safety concerns,
service conditions, and by local requirements. Means of joining if any, associated with its use. It is the responsibility of the user
or bending are also factors that affect the selection of the type of this standard to establish appropriate safety and health
of tube to be used.2 practices and determine the applicability of regulatory limita-
tions prior to use.
NOTE 1—Annealed tube is suitable for use with flared or compression
fittings, and with solder-type fittings, provided rounding and sizing of the 2. Referenced Documents
tube ends is performed where needed.
NOTE 2—Drawn temper tube is suitable for use with solder-type fittings. 2.1 The following documents of the issue in effect on date
Types A and B tube, in the drawn temper, are suitable for use with certain of material purchase form a part of this specification to the
types and sizes of compression fittings. extent referenced herein:
1.2 The tube shall be produced from the following coppers, 2.2 ASTM Standards:3
and the manufacturer has the option to supply any one of them, B32 Specification for Solder Metal
unless otherwise specified: B88 Specification for Seamless Copper Water Tube
Copper Previously Used Description B153 Test Method for Expansion (Pin Test) of Copper and
UNS No. Designation
Copper-Alloy Pipe and Tubing
C10200 OF Oxygen free without B577 Test Methods for Detection of Cuprous Oxide (Hydro-
residual deoxidants gen Embrittlement Susceptibility) in Copper
C12000 DLP Phosphorus deoxidized,
low residual phosphorus B601 Classification for Temper Designations for Copper and
C12200 DHP Phosphorus deoxidized, Copper Alloys—Wrought and Cast
high residual phosphorus B813 Specification for Liquid and Paste Fluxes for Solder-
1.3 The assembly of copper plumbing or fire sprinkler ing of Copper and Copper Alloy Tube
systems by soldering is described in Practice B828. B828 Practice for Making Capillary Joints by Soldering of
1.4 Solders for joining copper potable water or fire sprinkler Copper and Copper Alloy Tube and Fittings
systems are covered by Specification B32. The requirements B846 Terminology for Copper and Copper Alloys
for acceptable fluxes for these systems are covered by Speci- B900 Practice for Packaging of Copper and Copper Alloy
fication B813. Mill Products for U.S. Government Agencies
E2 Methods of Preparation of Micrographs of Metals and
Alloys (Including Recommended Practice for Photogra-
1
This specification is under the jurisdiction of ASTM Committee B05 on Copper
phy As Applied to Metallography); Replaced by E 883
and Copper Alloys and is the direct responsibility of Subcommittee B05.04 on Pipe (Withdrawn 1983)4
and Tube.
Current edition approved Oct. 1, 2013. Published November 2013. Originally
3
approved in 1983. Last previous edition approved in 2011 as B88M – 05 (2011). For referenced ASTM standards, visit the ASTM website, www.astm.org, or
DOI: 10.1520/B0088M-13. contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
2
The UNS system for copper and copper alloys (see Practice E527) is a simple Standards volume information, refer to the standard’s Document Summary page on
expansion of the former standard designation system accomplished by the addition the ASTM website.
4
of a prefix “C” and a suffix “00.” The suffix is permitted to be used to accommodate The last approved version of this historical standard is referenced on
composition variations of the base alloy. www.astm.org.

*A Summary of Changes section appears at the end of this standard

Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States

Copyright by ASTM Int'l (all rights reserved); 1

 B88M − 13
E3 Guide for Preparation of Metallographic Specimens 4.1.1 ASTM designation and year of issue (for example,
E8/E8M Test Methods for Tension Testing of Metallic Ma- B88M – 03),
terials 4.1.2 Copper UNS No. (not necessary unless a specific
E18 Test Methods for Rockwell Hardness of Metallic Ma- copper is desired),
terials 4.1.3 Nominal or standard size (Column 1 of Table 1) and
E29 Practice for Using Significant Digits in Test Data to whether Type A, B, or C (Section 3),
Determine Conformance with Specifications 4.1.4 Temper (Section 7),
E53 Test Method for Determination of Copper in Unalloyed 4.1.5 Length (see 11.5),
Copper by Gravimetry 4.1.6 How furnished: straight or coils,
E62 Test Methods for Chemical Analysis of Copper and 4.1.7 Quantity (pieces) of each size and type,
Copper Alloys (Photometric Methods) (Withdrawn 2010)4 4.1.8 In addition, when material is purchased for agencies of
E112 Test Methods for Determining Average Grain Size the U.S. Government, it shall conform to the Supplementary
E243 Practice for Electromagnetic (Eddy Current) Examina- Requirements as defined herein when specified in the contract
tion of Copper and Copper-Alloy Tubes or purchase order.
E255 Practice for Sampling Copper and Copper Alloys for
4.2 The following options are available and shall be speci-
the Determination of Chemical Composition
fied in the contract or purchase order when required:
E527 Practice for Numbering Metals and Alloys in the
4.2.1 Tension test (Section 8),
Unified Numbering System (UNS)
4.2.2 Grain size determination (Section 8),
3. Terminology 4.2.3 Expansion test (9.1), and
3.1 Definitions—For definitions of terms related to copper 4.2.4 Microscopical Examination for Hydrogen Embrittle-
and copper alloys, refer to Terminology B846. ment, Procedure B (9.3.2).

3.2 Definitions of Terms Specific to This Standard: 5. Materials and Manufacture

3.2.1 tube, copper water, n—a seamless copper tube con-
forming to the particular metric dimensions commercially 5.1 The material shall be of such quality and purity that the
known as Copper Water Tube and designated as Types A, B, finished product shall have the properties and characteristics
and C. prescribed in this specification, and shall be cold worked to
size.
4. Ordering Information 5.2 The tube shall be finished by such cold-working and
4.1 Include the following information for material ordered annealing operations as are necessary to produce the required
under this specification. temper and surface finish.

TABLE 1 Dimensions, Mass, and Tolerances in Diameter and Wall Thickness for Metric Copper Water Tube Sizes
(All tolerances are plus and minus except as otherwise indicated.)
Average Outside
Wall Thickness and Tolerances, mm Theoretical Mass, kg/m
Nominal or Outside DiameterA Tolerance, mm
Standard Diameter, Type A Type B Type C
Size, mm mm Annealed Drawn Wall Toler- Wall Toler- Wall Toler- Type A Type B Type C
Thickness anceB Thickness anceB Thickness anceB
C
6 6.0 0.05 0.03 0.80 0.08 0.70 0.07 0.60 0.117 0.104 0.091
C
8 8.0 0.05 0.03 0.90 0.09 0.80 0.08 0.60 0.179 0.162 0.125
C
10 10.0 0.05 0.03 0.90 0.09 0.80 0.08 0.60 0.230 0.207 0.158
12 12.0 0.06 0.03 1.2 0.1 0.90 0.09 0.60 0.06 0.364 0.280 0.192
15 15.0 0.06 0.03 1.2 0.1 1.0 0.1 0.70 0.07 0.465 0.393 0.281
18 18.0 0.06 0.03 1.2 0.1 1.0 0.1 0.70 0.07 0.566 0.477 0.340
22 22.0 0.06 0.03 1.6 0.15 1.1 0.1 0.80 0.08 0.917 0.646 0.476
28 28.0 0.07 0.04 1.6 0.15 1.2 0.1 0.90 0.09 1.19 0.903 0.685
35 35.0 0.10 0.04 1.6 0.15 1.4 0.15 1.1 0.1 1.50 1.32 1.05
42 42.0 0.10 0.05 1.8 0.2 1.5 0.15 1.2 0.1 2.03 1.71 1.37
54 54.0 0.10 0.05 2.1 0.2 1.7 0.15 1.5 0.15 3.06 2.50 2.21
67 67.0 0.12 0.05 2.4 0.25 2.0 0.2 1.6 0.15 4.35 3.65 2.94
79 79.0 0.12 0.05 2.8 0.3 2.3 0.25 1.8 0.2 5.99 4.95 3.90
105 105.0 0.12 0.05 3.4 0.35 2.8 0.3 2.4 0.25 9.70 8.04 6.92
130 130.0 0.12 0.05 4.0 0.4 3.1 0.3 2.7 0.25 14.2 11.0 9.65
156 156.0 0.12 0.05 4.8 0.5 3.5 0.35 3.1 0.3 20.3 15.0 13.3
206 206.0 0.15 + 0.05 6.8 0.7 5.0 0.5 4.3 0.45 38.0 28.2 24.4
−0.10
257 257.0 0.20 + 0.05 8.5 0.85 6.3 0.65 5.4 0.55 59.3 44.4 38.2
−0.15
308 308.0 0.20 + 0.05 10.3 1.0 7.1 0.7 6.4 0.65 86.1 60.0 54.2
−0.15
A
The average outside diameter of a tube is the average of the maximum and minimum outside diameter, as determined at any one cross section of the tube.
B
Maximum deviation at any one point.
C
Indicates that the material is not generally available or that no tolerance has been established.

Copyright by ASTM Int'l (all rights reserved); 2

 B88M − 13
5.3 Tube furnished in coils shall be annealed. flattened part. The tube so tested shall develop no cracks or
5.4 Tube furnished in straight lengths shall normally be in flaws visible to the unaided eye as a result of this test. In
the drawn temper. Upon agreement between the manufacturer making the flattening test the elements shall be slowly flattened
or supplier and the purchaser, the manufacturer shall have the by one stroke of the press.
option to supply annealed straight length tubing. 9.3 Microscopical Examination for Susceptibility to Hydro-
gen Embrittlement:
6. Chemical Composition 9.3.1 Tubes furnished in Copper UNS No. C10200 and
6.1 The material shall conform to the chemical composition C12000 shall be essentially free of cuprous oxide as deter-
requirements in Table 2 for the specific type of copper. mined by Procedure A of Test Methods B577. When Copper
6.2 These specification limits do not preclude the presence UNS No. C12200 is supplied, examination is not required. In
of other elements. When included in the contract or purchase case of a dispute, Procedure C of Test Methods B577 shall be
order, and agreed upon by the manufacturer or supplier and the used as the referee method.
purchaser, limits shall be established and analysis required for 9.3.2 Tubes furnished in all coppers shall be capable of
unnamed elements. passing the embrittlement test specified in Procedure B of Test
Methods B577. The actual performance of the test is not
7. Temper required unless specifically requested in the ordering docu-
7.1 The copper water tube shall be furnished in the tempers ment. In case of a dispute, Procedure C of Test Methods B577
designated below. Current designations as defined in Classifi- shall be used as the referee method.
cation B601 are as follows:
10. Nondestructive Testing
Annealed-O
Drawn-H 10.1 Eddy-Current Test—Each tube up to and including 79
8. Mechanical Properties mm in outside diameter shall be subjected to an eddy-current
test. Testing shall follow the procedure of Practice E243,
8.1 The tube shall conform to the mechanical property except the determination of “end effect” is not required. Tubes
requirements prescribed in Table 3. Tension tests and grain size shall be passed through an eddy current test unit adjusted to
determinations need not be made except when indicated by the provide information on the suitability of the tube for the
purchaser at the time of placing the order. A convenient method intended application.
of indicating that these tests are to be made is to state that “Test 10.1.1 The testing of tube of dimensions beyond the capa-
Procedure T is required” (see 4.2.1). Where agreement on the bilities of the eddy-current test apparatus shall be subject to
Rockwell hardness tests cannot be reached, the tensile strength negotiation between the producer and the purchaser.
and grain-size requirements of Table 3 shall be the basis for 10.1.2 Notch-depth standards, rounded to the nearest 0.03
acceptance or rejection. mm, shall be 22 % of the wall thickness. The notch-depth
9. Performance Requirements tolerance shall be 60.01 mm. Alternatively, at the option of the
manufacturer using speed insensitive eddy-current units that
9.1 Expansion Test—The annealed (O) tube shall be capable are equipped to select a fraction of the maximum unbalance
of being expanded in accordance with Test Method B153 with signal, the following percent maximum unbalance signals shall
an expansion of the outside diameter in the following amount: be used:
Nominal or Expansion of
Unbalance Signal
Standard Size, mm Outside Diameter, %
Nominal or Standard Tube Size, mm Magnitude, max %
15 and under 40
Up to and incl 12 0.2
Over 15 30
15 to 54, incl 0.3
The expanded tube shall show no cracking or rupture visible Over 54 to 79, incl 0.4
to the unaided eye. 10.1.3 Tubes that do not actuate the signalling device of the
9.2 Flattening Test—As an alternative to the expansion test eddy-current testers shall be considered as conforming to the
for tube standard sizes 105 mm and over in the annealed requirements of this test. Tubes with discontinuities indicated
condition, a section 100 mm in length shall be cut from the end by the testing unit shall, at the option of the manufacturer, be
of one of the lengths for a flattening test. This 100-mm test reexamined or retested to determine whether the discontinuity
specimen shall be flattened so that a gage set at three times the is cause for rejection. Signals that are found to have been
wall thickness will pass over the tube freely throughout the caused by minor mechanical damage, soil, or moisture shall not
be cause for rejection of the tubes provided the tube dimen-
sions are still within the prescribed limits and the tube is
TABLE 2 Chemical Composition—Weight %
suitable for its intended application.
Element Copper UNS No.
C10200A C12000 C12200
B
Copper, min 99.95 99.90 99.9 11. Dimensions, Mass, and Permissible Variations
Phosphorus ... 0.004–0.012 0.015–0.040
A
11.1 For the purpose of determining conformance with the
Oxygen shall be 10 ppm max.
B
Copper + silver. dimensional requirements prescribed in this specification, any
measured value outside the specified limiting values for any

Copyright by ASTM Int'l (all rights reserved); 3

 B88M − 13
TABLE 3 Mechanical Property Requirements
Temper Designation Rockwell HardnessA Tensile Strength, Average Grain Size,
Form
Standard Former Scale Value min, MPa mm
OS060 annealed coils F 50 max 200 0.040 min
OS035 annealed straight lengths F 55 max 200 0.025 min
H58 drawn drawn 30 T 30 min 250 ...
A
Rockwell hardness tests shall be made on the inside surfaces of the tube. When suitable equipment is not available for determining the specified Rockwell hardness,
other Rockwell scales and values shall be specified subject to agreement between the purchaser and the supplier.

TABLE 5 Nominal or Standard Lengths and Tolerances

dimensions shall make the tube subject to rejection at the Nominal or Standard Size,
Nominal or
Tolerance, mm
option of the purchaser. Type Standard
mm (all plus)
Length, m
11.2 Nominal or Standard Dimensions, Wall Thickness, and Tubes Furnished in Straight Lengths
Diameter Tolerances—The nominal or standard dimensions, Up to 206, incl A, B, C 6.0 25
257 B, C 6.0 25
wall thickness, and diameter tolerances shall be in accordance 257 A 5.5 25
with Table 1. 308 C 6.0 25
308 B 5.5 25
11.3 Mass—For purposes of calculating mass, cross 308 A 3.6 25
sections, and so forth, the density of the copper shall be taken Tubes Furnished in Coils
as 8.94 g/cm3. The theoretical mass per metre is shown in Table Up to 28, incl A, B 20 600
30 600
1. 35 and 42 A, B 20 600
54 A, B 12 600
11.4 Roundness—For drawn unannealed tube in straight 14 600
lengths, the roundness tolerance shall be as prescribed in Table
4. The deviation from roundness is measured as the difference
between major and minor diameters as determined at any one TABLE 6 Sampling Schedule
cross section of the tube. No roundness tolerance has been Number of Pieces in Lot Number of Sample Pieces to be TakenA
established for annealed tube in straight lengths or for tubes 1 to 50 1
furnished in coils. 51 to 200 2
201 to 1500 3
11.5 Lengths and Tolerances: Over 1500 0.2 % of total number of pieces in the lot
11.5.1 Standard Lengths and Tolerances—The standard but not more than 10 sample pieces
lengths and tolerances shall be as specified in Table 5. A
Each sample piece shall be taken from a separate tube.
11.5.2 Tube supplied in other than standard lengths and
tolerances shall be in accordance with requirements established
by agreement between the manufacturer or supplier and the
purchaser.
11.6 Squareness of Cut—For tube in straight lengths, the 14. Number of Tests and Retests
departure from squareness of the end of any tube shall not 14.1 Chemical Analysis—Samples for chemical analysis
exceed more than 0.25 mm for tube up to and including 15-mm shall be taken in accordance with Practice E255. Drillings,
standard size and not more than 0.40 mm/mm of outside millings, and so forth shall be taken in approximately equal
diameter for tube larger than 15-mm standard size. weight from each of the sample pieces selected in accordance
with 13.1 and combined into one composite sample. The
12. Workmanship, Finish, and Appearance
minimum weight of the composite sample that is to be divided
12.1 The material shall be clean, free of dirt and defects of into three equal parts shall be 150 g.
a nature that interfere with normal commercial applications.
14.1.1 Instead of sampling in accordance with Practice
13. Sampling E255, the manufacturer shall have the option of determining
conformance to chemical composition as follows: Confor-
13.1 Sample pieces shall be selected for test purposes from mance shall be determined by the manufacturer by analyzing
each lot of 5000 kg or fraction thereof, of each size and type,
samples taken at the time the castings are poured or samples
according to the schedule of Table 6.
taken from the semi finished product. If the manufacturer
determines the chemical composition of the material during the
course of manufacture, he shall not be required to sample and
TABLE 4 Roundness Tolerance
analyze the finished product. The number of samples taken for
Roundness Tolerance % of Out-
t/D (Ratio of Wall Thickness to
side Diameter (Expressed to
determination of chemical composition shall be as follows:
Outside Diameter)
Nearest 0.03 mm) 14.1.1.1 When samples are taken at the time the castings are
0.01 to 0.03, incl 1.5 poured, at least one sample shall be taken for each group of
Over 0.03 to 0.05, incl 1.0
Over 0.05 to 0.10, incl 0.8 castings poured simultaneously from the same source of
molten metal.

Copyright by ASTM Int'l (all rights reserved); 4

 B88M − 13
14.1.1.2 When samples are taken from the semi finished TABLE 7 Test Methods
product, a sample shall be taken to represent each 5000 kg or Test ASTM Designation
fraction thereof, except that not more than one sample shall be Chemical analysis E53, E62
required per piece. Tension E8/E8M (also see 15.2)
Rockwell hardness E18
14.1.1.3 Because of the discontinuous nature of the process- Grain size E2, E3, E112 (also see 15.3)
ing of castings into wrought products, it is not practical to Expansion (pin test) B153
Microscopical Examination, E3, B577 (also see 15.3)
identify specific casting analysis with a specific quantity of Procedure A
finished material. Microscopical Examination, E3, B577 (also see 15.3)
14.1.1.4 In the event that heat identification or traceability is Procedure B
required, the purchaser shall specify the details desired.
14.2 Mechanical Tests—For the mechanical tests, a speci-
men shall be taken from each of the sample pieces selected in 15.2.2 Whenever different tension test results are obtained
accordance with 13.1. The required mechanical test shall be from both full-size and from machined test specimens, the
made on each of the specimens so selected. The value for the results obtained from full-size test specimens shall be used to
Rockwell hardness number of each specimen shall be estab- determine conformance to the requirements of this specifica-
lished by taking the arithmetical average of at least three tion.
readings. 15.2.3 Tension test results on material covered by this
specification are not seriously affected by variations in speed of
14.3 Microscopical Examination—One specimen shall be testing. It is not prohibited to use a considerable range of
examined from each of the sample pieces selected in accor- testing speeds; however, the rate of stressing to the yield
dance with 13.1. strength shall not exceed 690 MPa/min. Above the yield
14.4 In the case of tube furnished in coils, a length sufficient strength, the movement per minute of the testing machine head
for all necessary tests shall be cut from each coil selected for under load shall not exceed 1.27 cm/cm of gage length (or
purpose of tests. The remaining portion of these coils shall be distance between grips for full-section specimens).
included in the shipment, and the permissible variations in 15.3 Grain Size and Microscopical Examination:
length of such coils shall be waived. 15.3.1 The specimen(s) shall be prepared in accordance
14.5 Retests: with Guide E3.
14.5.1 If any test specimen shows defective machining or 15.3.2 The surface of the test specimen shall approximate a
develops flaws, it shall be discarded and another specimen radial longitudinal section of the tube.
substituted.
16. Significance of Numerical Limits
14.5.2 If the results of any test made to determine the
mechanical properties fail to meet the specified requirements, 16.1 For purposes of determining compliance with the
two additional specimens shall be taken from different sample specified limits for requirements of the properties listed in
pieces and tested. The results of the tests on both of these Table 8, an observed value or calculated value shall be rounded
specimens shall meet the specified requirements. Failure of as indicated in accordance with the rounding method of
more than one specimen to meet the specified requirements for Practice E29.
a particular property shall be cause for rejection of the entire
17. Inspection
lot.
14.5.3 If the chemical analysis fails to conform to the 17.1 The manufacturer shall afford the inspector represent-
specified limits, analysis shall be made on a new composite ing the purchaser, all reasonable facilities to satisfy him that the
sample prepared from additional pieces selected in accordance tubes are being furnished in accordance with the specified
with 13.1. The results of this retest shall comply with the requirements.
specified requirements.
18. Rejection and Rehearing
15. Test Methods 18.1 Material that fails to conform to the requirements of
this specification is subject to rejection at the option of the
15.1 The properties enumerated in this specification shall, in
case of disagreement, be determined in accordance with the
ASTM methods listed in Table 7. TABLE 8 Rounding Units
Rounded Unit for Observed or
15.2 Tension Test: Property
Calculated Value
15.2.1 Tension test specimens shall be of the full section of Chemical composition nearest unit in the last right-hand place of
the tube and shall conform to the requirements of the section, Hardness figures of the specified limit
Specimens for Pipe and Tube, of Test Methods E8/E8M, unless
Tensile strength nearest 5 MPa
the limitations of the testing machine preclude the use of such Expansion nearest 1 %
a specimen. Use test specimens conforming to type No. 1 of Grain size:
Fig. 13, Tension Test Specimens for Large-Diameter Tubular Up to 0.055 mm, incl nearest multiple of 0.005 mm
Over 0.055 to 0.160 nearest 0.01 mm
Products, of Test Methods E8/E8M when a full-section speci- mm, incl
men cannot be tested.

Copyright by ASTM Int'l (all rights reserved); 5

 B88M − 13
purchaser. Rejection shall be reported to the manufacturer or not greater than 1 m. The legend shall include the type of the
supplier promptly and in writing. When requested by the tube, name or trademark of the manufacturer, or both, and the
manufacturer or supplier, a rehearing shall be granted. country of origin. The manufacturer has the option to include
other information.
19. Packaging and Package Marking
19.3.2 Colors used shall be green for Type A, blue for Type
19.1 The material shall be separated by size, composition, B, and red for Type C. Such color marking is not applicable to
and temper and prepared for shipment in such a manner as to tube furnished in annealed straight lengths or coils.
ensure acceptance by common carrier for transportation at the 19.3.3 UNS Copper Designation:
lowest rate applicable and to afford protection from the normal 19.3.3.1 Hard Drawn Tubing—On hard drawn tubing pro-
hazards of transportation. duced from C10200 and C12000, the UNS copper designation
19.2 Each shipping unit shall be legibly marked with the shall be identified at intervals not greater than 1 m with color
purchase order number, metal or alloy designation, temper, coded ink per 19.3.2.
size, total length or piece count, or both, and name of supplier. 19.3.3.2 Annealed Tubing—On annealed tubing produced
The specification number shall be shown, when specified. from C10200 and C12000, the UNS copper designation shall
19.3 Product Identification: be identified with ink or some other permanent mark that is
19.3.1 The name or trademark of the manufacturer and the repeated at intervals not greater than 1 m. Color marking to
mark indicative of the type shall be permanently (incised) distinguish Type A from Type B is not required.
marked on each tube at intervals not greater than 0.5 m. Tube
in straight lengths shall be further identified throughout its 20. Keywords
length by a colored marking of Xs, symbol, or logo not less 20.1 copper tube; seamless; UNS No. C10200; UNS No.
than 4.5 mm in height, including a legend repeated at intervals C12000; UNS No. C12200; water tube

SUPPLEMENTARY REQUIREMENTS

The following supplementary requirements shall apply only when specified by the purchaser in the
inquiry, contract, or order, for agencies of the U.S. Government.

S1. Referenced Documents requirements unless disapproved by the purchaser at the time
S1.1 The following documents of the issue in effect on date the order is placed. The purchaser shall have the right to
of material purchase form a part of this specification to the perform any of the inspections and tests set forth in this
extent referenced herein: specification when such inspections and tests are deemed
S1.1.1 Federal Standards:5 necessary to ensure that the material conforms to the prescribed
Fed. Std. No. 102 Preservation, Packaging and Packing requirements.
Levels S3. Identification Marking
Fed. Std. No. 123 Marking for Shipment (Civil Agencies)
S3.1 All material shall be properly marked for identification
Fed. Std. No. 146A Tolerances for Copper and Copper Base
in accordance with Fed. Std. No. 185 except that the ASTM
Alloy Mill Products
specification number and the alloy number shall be used.
Fed. Std. No. 185 Identification Marking of Copper and
Copper-Base Alloy Mill Products S4. Preparation for Delivery
S1.1.2 Military Standards:5
S4.1 Preservation, Packaging, Packing:
MIL-STD-105 Sampling Procedures and Tables for Inspec-
S4.1.1 Military Agencies—The material shall be separated
tion by Attributes
by size, composition, grade, or class and shall be preserved and
MIL-STD-129 Marking for Shipment and Storage
packaged, Level A or C, packed, Level A, B, or C, as specified
S2. Quality Assurance in the contract or purchase order, in accordance with the
requirements of Practice B900.
S2.1 Responsibility for Inspection: S4.1.2 Civil Agencies—The requirements of Fed. Std. No.
S2.1.1 Unless otherwise specified in the contract or pur- 102 shall be referenced for definitions of the various levels of
chase order, the manufacturer is responsible for the perfor- packaging protection.
mance of all inspection and test requirements specified. Except S4.2 Marking:
as otherwise specified in the contract or purchase order, the S4.2.1 Military Agencies—In addition to any special mark-
manufacturer has the option to use his own or any other ing required by the contract or purchase order, marking for
suitable facilities for the performance of the inspection and test shipment shall be in accordance with MIL-STD-129.
S4.2.2 Civil Agencies—In addition to any special marking
5
Available from DLA Document Services, Building 4/D, 700 Robbins Avenue, required by the contract or purchase order, marking for
Philadelphia, PA 19111-5094, http://quicksearch.dla.mil/. shipment shall be in accordance with Fed. Std. No. 123.

Copyright by ASTM Int'l (all rights reserved); 6

 B88M − 13

SUMMARY OF CHANGES

Committee B05 has identified the location of selected changes to this standard since the last issue
(B88M-05(2011)) that may impact its use:

(1) Removed definitions which have been defined in B846 (4) Deleted requirement in 5.3 Materials and Manufacture to
Standard Terminology for Copper and Copper Alloys. allow coils to be annealed prior to annealing.
(2) Made minor editorial corrections throughout the document. (5) In the Supplementary Requirements Section, removed ref-
(3) Made modifications to 10.1 Eddy-Current Test and to erence to withdrawn standard MIL-C-3993 and replaced with
14.5.2 Number of Tests and Retests to bring into line with reference to Practice B900.
Specification B88.

ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned
in this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk
of infringement of such rights, are entirely their own responsibility.

This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and
if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards
and should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of the
responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should
make your views known to the ASTM Committee on Standards, at the address shown below.

This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,
United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above
address or at 610-832-9585 (phone), 610-832-9555 (fax), or service@astm.org (e-mail); or through the ASTM website
(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222
Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http://www.copyright.com/

Copyright by ASTM Int'l (all rights reserved); 7